Tetradecanol dehydrogenation over CuO catalyst supported on BaO, CaO and MgO

Bimetallic Cu/Mg, Ca, Ba mixed oxide compounds acted as catalyst in the dehydrogenation of tetradecanol into tetradecanal, and were characterized by thermal gravimetric analysis, surface area, X-ray diffraction, temperature-programmed reduction and desorption of CO₂. Alkaline earth oxides increased the total basic site concentration in the order of Mg>Ca>Ba. A correlation was found between the total basic site concentration and initial dehydrogenation rate. This revised version was published online in June 2006 with corrections to the Cover Date.     

Dielectric properties of europium-indium oxide solid solution films prepared on Si (100) substrates

Thin Eu-In solid solution oxide films (SS) were grown on Si (P) substrates to form MOS devices. The samples were characterised by X-ray fluorescence and X-ray diffraction techniques. The ac-conductance and capacitance of the devices were studied as a function of frequency in the range 500 Hz to 100 kHz, temperature in the range 293-400 K and gate voltage. The investigation established that: (1) the prepared SS exhibit a sudden reversible structural change at about 370 K, (2) the frequency dependence for f>10 kHz of the ac-conductivity and capacitance of the insulator at room temperature is controlled by the ‘corrected barrier hopping’ CBH model, (3) the temperature dependence of the ac-conductance which shows a small activation energy characterises the hopping process of current carriers between equilibrium sites, and (4) the prepared transparent SS have a sufficiently high relative permittivity ?, around 30, which suggests they are promising candidates for high-? dielectric applications.     

Magnetic properties of lanthanum orthoferrite fine powders prepared by different chemical routes

Fine powders of lanthanum iron oxide, LaFeO₃, have been prepared by solid state reaction as well as sol-gel synthesis and nebulized spray pyrolysis. Structures, morphologies and magnetic susceptibility measurements of these powders have been examined. The powders prepared by all the three low-temperature routes contain nearly spherical particles with an average diameter of 40 nm. These samples show a lower Neel temperature than the powder prepared by solid state reaction besides showing much lower magnetic susceptibility at low temperatures. Dedicated to Professor C N R Rao on his 70th birthday     

K＋－SrO－La_2O_3／ZnO催化剂上甲烷氧化偶联反应Ⅰ．催化活性和反应气中添加CO_2的影响

Ｋ＋┐ＳｒＯ┐Ｌａ２Ｏ３／ＺｎＯ催化剂上甲烷氧化偶联反应＊Ⅰ．催化活性和反应气中添加ＣＯ２的影响余林徐奕德＊＊郭燮贤（中国科学院大连化学物理研究所催化基础国家重点实验室，大连１１６０２３）关键词钾离子，氧化锶，氧化镧，氧化锌，金属氧化物催化剂，甲烷，...     

三甲基膦和环氧乙烷的加成产物裂解反应机理的MNDO法研究

文中用ＭＮＤＯ方法研究了三甲基膦和环氧乙烷加成产物裂解反应机理     

Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

Preparation and characterization of iron oxide thin films by spray pyrolysis using methanolic and ethanolic solutions

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; α-Fe₂O₃ thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of 10⁵ cm⁻¹. The optical band gap of films was found to be 2.26 and 2.20 eV for the films deposited using methanolic and ethanolic solutions, respectively.     

Synthesis and properties of triethylammonium 2,2,5-triphenyl-1,3,2,5-dioxaborataphosphorinane

The reaction of bis(hydroxymethyl)phenylphosphine with isobutyl diphenylborate in the presence of triethylamine leads to the formation of triethylammonium 2,2,5-triphenyl-1,3,2,5-dioxaborataphosphorinane (1). The reaction of compound 1 with electrophilic reagents (O, S, Se, CH₂O, RHal) leads to quaternization of the phosphorus atom, giving the corresponding phosphine oxides, sulfides, and selenides and P,B-containing betaines. In the reactions of compound 1 with amines aminomethylphosphines of the diazaphosphorinane and diazadiphosphacyclooctane series are formed. Ammonium 1,3,2,5-dioxaborataphosphorinanes dissociate in solutions and enter into ion exchange with phosphonium iodides, leading to phosphonium 1,3,2,5-dioxaborataphosphorinanes. The latter, in the case of the aminomethylphosphonium cation, undergo intramolecular rearrangement with the formation of P,B-containing betaines and aminomethylphosphines.Deceased.A. E. Arbuzov Institute of Organic and Physical Chemistry, Kazan' Scientific Center, Russian Academy of Sciences, 420083 Kazan'. Translated fromIzvestiya Akademii Nauk, Seriya Khimicheskaya, No. 6, pp. 1398–1405, June, 1992.     

Tuning size and catalytic activity of nano-clusters of cobalt oxide

Cobalt oxides were prepared by three different methods: (1) by reacting cobalt nitrate with oxalic acid, (2) co-precipitating cobalt nitrate with sodium carbonate, and (3) using sodium dodecyl sulphate as organic surfactant. All three samples were characterized before and after calcination by solvent extraction and the resulting products examined by IR spectroscopy. In the case of method 3, the removal of surfactant was followed by TGA studies. Products from all three methods were identified by XRD. Peaks in low angle XRD indicate the porous nature of the oxides. The morphology of the pores was studied by transmission electron microscopy. Some irregular pore structures were obtained for samples from methods 1 and 2, with an average size of 4–6 nm. Only the product from method 3 using SDS as template showed ordered structure and optimum size, and Brunauer-Emmet-Teller surface areas of the as-prepared, as well as the treated samples, exhibited H3 type hysteresis. The samples from the three methods were used as catalysts in the oxidation reaction of cyclohexane under mild conditions and the catalytic efficiency of the cobalt oxide was comparable with mesoporous cobalt oxides.     

Orientation and relaxation of polymer–clay solutions studied by rheology and small-angle neutron scattering

The influence of shear on viscoelastic solutions of poly(ethylene oxide) (PEO) and clay [montmorillonite, i.e., Cloisite NA+ (CNA)] was investigated with rheology and small-angle neutron scattering (SANS). The steady-state viscosity and SANS were used to measure the shear-induced orientation and relaxation of the polymer and clay platelets. Anisotropic scattering patterns developed at much lower shear rates than in pure clay solutions. The scattering anisotropy saturated at low shear rates, and the CNA clay platelets aligned with the flow, with the surface normal parallel to the gradient direction. The cessation of shear led to partial and slow randomization of the CNA platelets, whereas extremely fast relaxation was observed for laponite (LRD) platelets. These PEO–CNA networklike solutions were compared with previously reported PEO–LRD networks, and the differences and similarities, with respect to the shear orientation, relaxation, and polymer–clay interactions, were examined. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3102–3112, 2004